Desorption behavior of a surfactant in a linear low‐density polyethylene blend at elevated temperatures

The desorption behavior of a surfactant in a linear low‐density polyethylene (LLDPE) blend at elevated temperatures of 50, 70, and 80 °C was studied with Fourier transform infrared spectroscopy. The composition of the LLDPE blend was 70:30 LLDPE/low‐density polyethylene. Three different specimens (II, III, and IV) were prepared with various compositions of a small molecular penetrant, sorbitan palmitate (SPAN‐40), and a migration controller, poly(ethylene acrylic acid) (EAA), in the LLDPE blend. The calculated diffusion coefficient (D) of SPAN‐40 in specimens II, III, and IV, between 50 and 80 °C, varied from 1.74 × 10^?11 to 6.79 × 10^?11 cm²/s, from 1.10 × 10^?11 to 5.75 × 10^?11 cm²/s, and from 0.58 × 10^?11 to 4.75 × 10^?11 cm²/s, respectively. In addition, the calculated activation energies (E_D) of specimens II, III, and IV, from the plotting of ln D versus 1/T between 50 and 80 °C, were 42.9, 52.7, and 65.6 kJ/mol, respectively. These values were different from those obtained between 25 and 50 °C and were believed to have been influenced by the interference of Tinuvin (a UV stabilizer) at elevated temperatures higher than 50 °C. Although the desorption rate of SPAN‐40 increased with the temperature and decreased with the EAA content, the observed spectral behavior did not depend on the temperature and time. For all specimens stored over 50 °C, the peak at 1739 cm^?1 decreased in a few days and subsequently increased with a peak shift toward 1730 cm^?1. This arose from the carbonyl stretching vibration of Tinuvin, possibly because of oxidation or degradation at elevated temperatures. In addition, the incorporation of EAA into the LLDPE blend suppressed the desorption rate of SPAN‐40 and retarded the appearance of the 1730 cm^?1 peak. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1114–1126, 2004     

Bio‐based nanocomposites from functionalized plant oils and layered silicate

Some discovery work was done on the synthesis of clay nanocomposites based on renewable plant oils. Functionalized triglycerides, such as acrylated epoxidized soybean oil, maleinized acrylated epoxidized soybean oil, and soybean oil pentaerythritol maleates, combined with styrene were used as the polymer matrix. The miscibility of these monomers and clay organomodifier was assessed by solubility parameters. The formation of nanocomposites was confirmed by both X‐ray data and transmission electron microscopy. The morphology showed a mix of intercalated and partially exfoliated sheets. The flexural modulus increased 30% at only 4 vol % clay content, but there was no significant effect on flexural strength, glass‐transition temperature, and thermal stability. Property enhancement was related to the degree of exfoliation that depends on both the polarity and flexibility of the monomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1441–1450, 2004     

Colorimetric recognition of different enzymology-concerning transition metals based on a hybrid cluster complex.

A hybrid cluster complex, formed by chelating a chromogenic ligand to a [2Fe-2S] cluster, sensitively exhibited differential colorimetric responses towards Hg2+, Cd2+, Cr3+, Pb2, Sn2+, Cu2+, Zn2+, Fe3+ and Co2+ in water at physiological pH. Speciation of some of these metal elements, such as Cr(III) and Sn(IV), was also studied by UV/Vis absorption.     

高功率LDA紧密侧面抽运Nd:YLF两级双程离轴放大系统实验研究

 介绍了一台10mm口径两级双程离轴放大系统，实现了对5mm×5mm口径光束的激光放大，耦合系统采用高功率LDA紧密侧面直接抽运棒状Nd:YLF方式。分析并实验研究了在不同抽运电流、放大脉冲与放大器LDA抽运时刻的不同延时及不同注入能量条件下，放大系统及光束每次放大时放大特性的规律。实验得到：在放大系统5mm×5mm软光阑处注入1.58mJ能量时，放大系统可输出129.2mJ能量，能量提取效率达到19.5%，满足该系统的设计指标。     

光学非球面二次曲面常数及顶点曲率的研究

受光学非球面制造过程中诸工艺参数的影响,能否保证非球面顶点曲率及二次曲面常数的精度是一个重要问题。基于二次曲面方程,推导出确定光学非球面二次曲面常数k以及顶点曲率半径r的一组算法,并在对一块口径为760mm×200mm标准非球面反射镜的实际测算中进行拟合,经过优化,拟合精度达到Δk=0.015,Δr=0.341mm,从而有效的控制了光学非球面制造过程中的顶点曲率及二次曲面常数的偏差。     

波段三维ESR成像系统的研制（Ⅴ）——灵敏度与分辨率实验及系统总性能指标

实验确定了自行研制的L波段三维电子自旋共振成像（3D-ESRI）系统的检测灵敏度及成像分辨率指标. 用Tempo水溶液模型测量灵敏度结果表明： 样品体积为10 mm, 高30 mm，测量浓度1×10^-4 mol/L水溶液的信噪比为S/N=4∶1；加梯度磁场后，样品浓度需>5×10^-4 mol/L，样品体积为19 mm, 高30 mm时，获得的投影谱的信噪比可满足图像重建的需要. 用DPPH固体样品确定的成像分辨率结果<1 mm. 文中还对ESRI系统的
各项总体性能做了归纳总结.     

Zn(BTZ)2白色有机电致发光材料的合成及其器件制备

以PCl₃为脱水剂,将邻氨基硫酚与水杨酸脱水环化合成出2-(2-羟基苯基)苯并噻唑,并进一步将所得产物与乙酸锌反应合成出2-(2-羟基苯基)苯并噻唑螯合锌(Zn(BTZ)₂)材料。以该配合物作为发光层制备出结构为ITO/PVK:TPD/Zn(BTZ)₂/Al近白色电致发光器件,其色坐标位于白场之内(x=0.242,y=0.359),在驱动电压为16V时,亮度达3200cdm²,对应的量子效率为0.32%。进一步在Zn(BTZ)₂中掺入橙红色染料Rubrene,制成ITO/PVK:TPD/Zn(BTZ)₂:Rubrene/Al结构器件,实现了纯白色发光(色坐标值:x=0.324,y=0.343),非常接近于白色等能点,且量子效率达0.47%。最后对上述器件的发光和电学性能进行了深入的研究和探讨。     

爆磁压缩发生器通过脉冲变压器对脉冲形成线充电的理论分析

 将爆磁压缩等效为电流源的方法，对爆磁压缩发生器通过脉冲变压器对脉冲形成线充电进行了理论分析，得出爆磁压缩发生器在负载上产生电流波形（简称负载电流）为直线情况和任意电流波形情况下充电电流和充电电压的表达式。分析表明变压器耦合互感与负载电流随时间变化增长率是脉冲形成线充电的两个重要参数，脉冲形成线第一个充电电压峰值与变压器的耦合互感和负载电流波形斜率成正比，负载电流波形斜率的变化可以改变充电电压峰值的时间，斜率不断增加可以延长第一个充电电压峰值时间，从而可能增加充电电压的幅值，提高爆磁压缩发生器能量的利用效率。     

Synthesis of Cationic PEM Emulsion and Application in Waste Water Treatment

Cationic polymer as a kind of flocculant is widely applied in purification treatment of waste water. Because it has positive charge group, it is able to connect strongly the suspended matters, short cellulose and other microparticles. The research on synthesis of cationic polymer and application in treatment of waste water is very universal abroad. But domestic research on those is not general. The technology of synthesis of PEM is simple, and the production cost is low. It is easy to apply in treatment of waste water.Synthesis of PEM Emulsion FlocculantSome distilled water, PVA(poly(vinyl alcohol)), EA(ethyl acrylate), and K2S2O8(potassium persulfate) were put into reaction vessel. Kept stirring up under nitrogen. When heated the solution to 40℃, dropped the water solution of MTA[(2-methacryloxylethyl)trimethyl ammonium].Maintained the temperature at 70℃, reacted about 7-8 hours. Then got the PEM emulsion. Changed the ratio of EA and MTA. Obtained a series of PEM emulsions.Stability and Convertibility of PEM EmulsionThe test results showed that when the EA/MTA was 85/15, the PEM emulsion was most stable.When the total monomer quantity was 35%, the convertibility of PEM emulsion was the highest,i.e.98.6%.The MTA Copolymerization Ratio and Morphology of PEM EmulsionWhen the monomers EA/MTA=85/15 and total monomer quantity was 35%, the MTA copolymerization ratio of PEM emulsion was 95.15%(the highest), and the PEM emulsion was some microspheres with 100-180nm of diameter.The Test Results of PEM Emulsion in Treatment of Waste Water The PEM emulsion flocculant was applied in treatment of waste water of paper mill, and measured the precipitation time(t) and transmittancy(T). The test results were showed in table 1. The optimum value of PEM which was able to make the waste water of paper mill into clear water was 0.008%.     

The Research on Polymer Microcapsulation for Cell Technology

Microcapsulation is a technology that enwrapped the solid or liquid or some gas matter with membrane materials to form microparticles(i.e.microcapsules). The materials of microcapsule is composed of naturnal polymers or modified naturnal polymers or synthesized polymers. The water-soluble core matter can only use oil-soluble wall materials, and vice versa.Synthesized methods of polymer microcapsulesSynthesized methods with monomers as raw materialsThis kind of methods include suspension polymerization, emulsion polymerization, dispersal polymerization, precipitation polymerization,suspension condensation polymerization, dispersal condensation polymerization, deposition condensation polymerization, interface condensation polymerization, and so on.Synthesized methods with polymers as raw materialsThese methods are suspension cross-linked polymerization, coacervation phase separation,extraction with solvent evaporation, polymer deposition, polymer chelation, polymer gel,solidification of melting polymer, tray-painted ways, fluidized bed ways, and so forth.Polymer materials to synthesize microcapsules2.1. Naturnal polymer materialsThe characteristics of this kind of materials are easy to form membrane, good stability and no toxicity. The polymer materials include lipids(liposome), amyloses, proteins, plant gels, waxes, etc.2.2. Modified polymer materialsThe characteristics of these materials are little toxicity, high viscidity(viscosity), soluble salt materials. But they cannot be used in water, acidic environment and high temperature environment for a long time. The materials include all kind of derivants of celluloses.2.3. Synthesized polymer materialsThe characteristics of the materials are easy to form membrane, good stability and adjustment of membrane properties. The synthesized polymer materials include degradable polymers(PLA, PGA,PLGA, PCL, PHB, PHV, PHA, PEG, PPG and the like) and indegradable polymers(PA, PMMA,PAM, PS, PVC, PB, PE, PU, PUA, PVA and otherwise).The applications of polymer microcapsules in cell technologyThe "artificial cell" is the biological active microcapsule used in biological and medical fields.The applications of cells (including transgenic cells, the same as artificial cells) technology include several aspects as follows:3.1. Microcapsulation of artificial red cell3.2. Microcapsule of artificial cell of biological enzyme3.3. Microcapsule of artificial cell of magnetic material3.4. Microcapsule of artificial cell of active carbon3.5. Microcapsule of active biological cell